9783846511466 - High Strength Polymer Fly ash Composites: Fundamental Understanding de Nath, Dilip; Bandyopadhyay, Sri (9 resultados)

Condición: New. pp. 292.

Taschenbuch. Condición: Neu. High Strength Polymer Fly ash Composites | Fundamental Understanding | Dilip Nath (u. a.) | Taschenbuch | 292 S. | Englisch | 2011 | LAP LAMBERT Academic Publishing | EAN 9783846511466 | Verantwortliche Person für die EU: BoD - Books on Demand, In de Tarpen 42, 22848 Norderstedt, info[at]bod[dot]de | Anbieter: preigu.

Paperback. Condición: Like New. LIKE NEW. SHIPS FROM MULTIPLE LOCATIONS. book.

Taschenbuch. Condición: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -The content of the book can be divided into two different types of composites based on the nature of polymer used: i) Hydrocarbon based Polymer (Polypropylene, PP) and fly ash, ii) Functionalized-Polymer (Polyvinyl alcohol, PVA) and fly ash. Composites of Gladstone fly ash (GFA) reinforced isotactic semicrystalline PP were prepared by injection molding at 210 °C incorporating 20, 45 and 60 wt% GFA. Tensile tests were carried out at 25, 50 and 70 °C. Modulus of elasticity of all composites at all temperatures was higher than that of the corresponding PP samples the gain ranged between 10 to 60 %. The strength of the composites had a mixed trend. Biodegradable composite films of PVA and Swanbank fly ash (SFA) spanning 5, 10, 15, 20 and 25 wt% concentrations were prepared by casting aqueous solutions. Four different classes of composite films were prepared by PVA and SFA. The tensile strengths of the composite films were increased proportionally via addition of SFA. The strength of the film was enhanced by 193 % with 20 wt% SFA compared to the neat PVA control. Further addition of SFA deviated from the linear trend. 292 pp. Englisch.

Condición: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Nath DilipDilip Nath, DEng, PhD- Research Associate, School of Materials Science and Engineering, The University of New South Wales, Australia. He published another book under title, Synthesis of Carbon Nanotubes: Fly ash as Catalys.

Condición: New. Print on Demand pp. 292 2:B&W 6 x 9 in or 229 x 152 mm Perfect Bound on Creme w/Gloss Lam.

Condición: New. PRINT ON DEMAND pp. 292.

Taschenbuch. Condición: Neu. This item is printed on demand - Print on Demand Titel. Neuware -The content of the book can be divided into two different types of composites based on the nature of polymer used: i) Hydrocarbon based Polymer (Polypropylene, PP) and fly ash, ii) Functionalized-Polymer (Polyvinyl alcohol, PVA) and fly ash. Composites of Gladstone fly ash (GFA) reinforced isotactic semicrystalline PP were prepared by injection molding at 210 °C incorporating 20, 45 and 60 wt% GFA. Tensile tests were carried out at 25, 50 and 70 °C. Modulus of elasticity of all composites at all temperatures was higher than that of the corresponding PP samples - the gain ranged between 10 to 60 %. The strength of the composites had a mixed trend. Biodegradable composite films of PVA and Swanbank fly ash (SFA) spanning 5, 10, 15, 20 and 25 wt% concentrations were prepared by casting aqueous solutions. Four different classes of composite films were prepared by PVA and SFA. The tensile strengths of the composite films were increased proportionally via addition of SFA. The strength of the film was enhanced by 193 % with 20 wt% SFA compared to the neat PVA control. Further addition of SFA deviated from the linear trend.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 292 pp. Englisch.

Taschenbuch. Condición: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - The content of the book can be divided into two different types of composites based on the nature of polymer used: i) Hydrocarbon based Polymer (Polypropylene, PP) and fly ash, ii) Functionalized-Polymer (Polyvinyl alcohol, PVA) and fly ash. Composites of Gladstone fly ash (GFA) reinforced isotactic semicrystalline PP were prepared by injection molding at 210 °C incorporating 20, 45 and 60 wt% GFA. Tensile tests were carried out at 25, 50 and 70 °C. Modulus of elasticity of all composites at all temperatures was higher than that of the corresponding PP samples the gain ranged between 10 to 60 %. The strength of the composites had a mixed trend. Biodegradable composite films of PVA and Swanbank fly ash (SFA) spanning 5, 10, 15, 20 and 25 wt% concentrations were prepared by casting aqueous solutions. Four different classes of composite films were prepared by PVA and SFA. The tensile strengths of the composite films were increased proportionally via addition of SFA. The strength of the film was enhanced by 193 % with 20 wt% SFA compared to the neat PVA control. Further addition of SFA deviated from the linear trend.