anna kario (5 resultados)

Taschenbuch. Condición: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -1. The optimum solution for the difficulties during conductor deformation was to use the ex situ precursor powder which is not sensitive to heat treatments in the range of temperatures needed for the working stress release of the sheath metal. Two different ex situ powders are studied: homemade ex situ (based on mechanically alloyed in situ powder) and commercial powder with reduced crystallite size achieved by high energy ball milling.2. As the first approach, ex situ powder is prepared using mechanical alloying. A detailed phase analysis shown secondary phases, such as MgO and MgB4+x. A high critical current density for unsintered tapes and wires was obtained. It is observed that non of the applied final heat treatments of the conductors improve their superconducting properties. It is assumed that, heat treatments influence the crystallite size which is explained by MgO at the grain boundaries blocking grain growth. Additional milling or chemical treatment of the powder to clean the grains is needed to accomplish a smaller particle size. However, if medium Jc values are sufficient, the MA in-ex situ powder is an interesting precursor powder for conductors needed for the react & wind method of superconducting coil preparation, because the final heat treatment of a such a conductor is not needed. 120 pp. Englisch.

Kartoniert / Broschiert. Condición: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Klappentextrnrn1. The optimum solution for the difficulties during conductor deformation was to use the ex situ precursor powder which is not sensitive to heat treatments in the range of temperatures needed for the working stress release of the .

Taschenbuch. Condición: Neu. This item is printed on demand - Print on Demand Titel. Neuware -1. The optimum solution for the difficulties during conductor deformation was to use the ex situ precursor powder which is not sensitive to heat treatments in the range of temperatures needed for the working stress release of the sheath metal. Two different ex situ powders are studied: homemade ex situ (based on mechanically alloyed in situ powder) and commercial powder with reduced crystallite size achieved by high energy ball milling.2. As the first approach, ex situ powder is prepared using mechanical alloying. A detailed phase analysis shown secondary phases, such as MgO and MgB4+x. A high critical current density for unsintered tapes and wires was obtained. It is observed that non of the applied final heat treatments of the conductors improve their superconducting properties. It is assumed that, heat treatments influence the crystallite size which is explained by MgO at the grain boundaries blocking grain growth. Additional milling or chemical treatment of the powder to clean the grains is needed to accomplish a smaller particle size. However, if medium Jc values are sufficient, the MA in-ex situ powder is an interesting precursor powder for conductors needed for the react & wind method of superconducting coil preparation, because the final heat treatment of a such a conductor is not needed.Cuvillier Verlag, Nonnenstieg 8, 37075 Göttingen 120 pp. Englisch.

Taschenbuch. Condición: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - 1. The optimum solution for the difficulties during conductor deformation was to use the ex situ precursor powder which is not sensitive to heat treatments in the range of temperatures needed for the working stress release of the sheath metal. Two different ex situ powders are studied: homemade ex situ (based on mechanically alloyed in situ powder) and commercial powder with reduced crystallite size achieved by high energy ball milling.2. As the first approach, ex situ powder is prepared using mechanical alloying. A detailed phase analysis shown secondary phases, such as MgO and MgB4+x. A high critical current density for unsintered tapes and wires was obtained. It is observed that non of the applied final heat treatments of the conductors improve their superconducting properties. It is assumed that, heat treatments influence the crystallite size which is explained by MgO at the grain boundaries blocking grain growth. Additional milling or chemical treatment of the powder to clean the grains is needed to accomplish a smaller particle size. However, if medium Jc values are sufficient, the MA in-ex situ powder is an interesting precursor powder for conductors needed for the react & wind method of superconducting coil preparation, because the final heat treatment of a such a conductor is not needed.

Taschenbuch. Condición: Neu. High Energy Milled Ex situ MgB2 for Tapes and Wires | Anna Kario | Taschenbuch | Englisch | 2011 | Cuvillier | EAN 9783869557328 | Verantwortliche Person für die EU: Cuvillier Verlag, Nonnenstieg 8, 37075 Göttingen, info[at]cuvillier[dot]de | Anbieter: preigu Print on Demand.