ISBN: 9783846581186 - wear behavior: some detonation gun sprayed coatings on grey cast iron (5 resultados)

Taschenbuch. Condición: Neu. Wear Behavior | Some Detonation Gun Sprayed Coatings on Grey Cast Iron | Vikas Chawla (u. a.) | Taschenbuch | 76 S. | Englisch | 2012 | LAP LAMBERT Academic Publishing | EAN 9783846581186 | Verantwortliche Person für die EU: BoD - Books on Demand, In de Tarpen 42, 22848 Norderstedt, info[at]bod[dot]de | Anbieter: preigu.…

Taschenbuch. Condición: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Wear problem of grey cast irons selected as case study in this work is being faced in Brake Rotors, where abrasive and adhesive wear of these grey cast irons takes place due to the abrasive action. Although efforts have been made to reduce the friction coefficient and to increase the wear resistance of grey cast irons by varying alloying elements such as titanium yet there is little or no work on the use of coatings on various grades of grey cast irons used in braking rotors. The objective of the study is to develop the Detonation Sprayed wear resistant coatings Cylindrical pins of grey iron (GIHC and GI250) have been prepared. Three different coatings i.e. Stellite-21, Cr3C-25NiCr, and Al2O3-40TiO2 were deposited on end faces of these pins. Coatings were characterized using SEM/EDAX and XRD analysis. The wear testing on the uncoated as well as coated grey cast iron specimens was done with the help of Pin-on- Disk wear test rig. Wear data was collected for three loads i.e. 40N, 50N, 60N. The worn out specimens were characterized by SEM / EDXA analyses. 76 pp. Englisch. …

Taschenbuch. Condición: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Wear problem of grey cast irons selected as case study in this work is being faced in Brake Rotors, where abrasive and adhesive wear of these grey cast irons takes place due to the abrasive action. Although efforts have been made to reduce the friction coefficient and to increase the wear resistance of grey cast irons by varying alloying elements such as titanium yet there is little or no work on the use of coatings on various grades of grey cast irons used in braking rotors. The objective of the study is to develop the Detonation Sprayed wear resistant coatings Cylindrical pins of grey iron (GIHC and GI250) have been prepared. Three different coatings i.e. Stellite-21, Cr3C-25NiCr, and Al2O3-40TiO2 were deposited on end faces of these pins. Coatings were characterized using SEM/EDAX and XRD analysis. The wear testing on the uncoated as well as coated grey cast iron specimens was done with the help of Pin-on- Disk wear test rig. Wear data was collected for three loads i.e. 40N, 50N, 60N. The worn out specimens were characterized by SEM / EDXA analyses.…

Condición: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Chawla VikasDirector / Principal (Bhai Maha Singh College of Engg. INDIA)Young Scientist & Best Engg. College Teacher Awardee PhD: I.I.T. Roorkee, INDIA Supervised numerous UG & PG Research Projects Publications: 72: Internationa.…

Taschenbuch. Condición: Neu. This item is printed on demand - Print on Demand Titel. Neuware -Wear problem of grey cast irons selected as case study in this work is being faced in Brake Rotors, where abrasive and adhesive wear of these grey cast irons takes place due to the abrasive action. Although efforts have been made to reduce the friction coefficient and to increase the wear resistance of grey cast irons by varying alloying elements such as titanium yet there is little or no work on the use of coatings on various grades of grey cast irons used in braking rotors. The objective of the study is to develop the Detonation Sprayed wear resistant coatings Cylindrical pins of grey iron (GIHC and GI250) have been prepared. Three different coatings i.e. Stellite-21, Cr3C-25NiCr, and Al2O3-40TiO2 were deposited on end faces of these pins. Coatings were characterized using SEM/EDAX and XRD analysis. The wear testing on the uncoated as well as coated grey cast iron specimens was done with the help of Pin-on- Disk wear test rig. Wear data was collected for three loads i.e. 40N, 50N, 60N. The worn out specimens were characterized by SEM / EDXA analyses.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 76 pp. Englisch.…