Artículos relacionados a Study on the Effect of Grain Refiner: On Microstructure...
Study on the Effect of Grain Refiner: On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications - Tapa blanda
Sinopsis
Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490℃ for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm.
"Sinopsis" puede pertenecer a otra edición de este libro.
Comprar nuevo
Ver este artículo
EUR 43,90
EUR 11,00 gastos de envío desde Alemania a España
Destinos, gastos y plazos de envíoResultados de la búsqueda para Study on the Effect of Grain Refiner: On Microstructure...
Imagen de archivo
Study on the Effect of Grain Refiner
Publicado por
LAP LAMBERT Academic Publishing Sep 2022, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Taschenbuch
Librería: BuchWeltWeit Ludwig Meier e.K., Bergisch Gladbach, Alemania
Calificación del vendedor: 5 de 5 estrellas
Taschenbuch. Condición: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490 for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm. 52 pp. Englisch. Nº de ref. del artículo: 9786205499849
Cantidad disponible: 2 disponibles
Imagen del vendedor
Study on the Effect of Grain Refiner
Publicado por
LAP LAMBERT Academic Publishing, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Tapa blanda
Librería: moluna, Greven, Alemania
Calificación del vendedor: 4 de 5 estrellas
Condición: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Singha PrasenjitM-tech IIT Kharagpur, research scholar IIT Madras.Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold roll. Nº de ref. del artículo: 731805322
Cantidad disponible: Más de 20 disponibles
Imagen de archivo
Study on the Effect of Grain Refiner : On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications
Publicado por
LAP LAMBERT Academic Publishing, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Taschenbuch
Librería: AHA-BUCH GmbH, Einbeck, Alemania
Calificación del vendedor: 5 de 5 estrellas
Taschenbuch. Condición: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490 for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm. Nº de ref. del artículo: 9786205499849
Cantidad disponible: 1 disponibles
Imagen de archivo
Study on the Effect of Grain Refiner: On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications
Publicado por
LAP LAMBERT Academic Publishing, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Tapa blanda
Librería: Majestic Books, Hounslow, Reino Unido
Calificación del vendedor: 5 de 5 estrellas
Condición: New. Print on Demand. Nº de ref. del artículo: 400120514
Cantidad disponible: 4 disponibles
Imagen de archivo
Study on the Effect of Grain Refiner: On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications
Publicado por
LAP LAMBERT Academic Publishing, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Tapa blanda
Librería: Books Puddle, New York, NY, Estados Unidos de America
Calificación del vendedor: 4 de 5 estrellas
Condición: New. Nº de ref. del artículo: 26397337885
Cantidad disponible: 4 disponibles
Imagen de archivo
Study on the Effect of Grain Refiner: On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications
Publicado por
LAP LAMBERT Academic Publishing, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Tapa blanda
Librería: Biblios, Frankfurt am main, HESSE, Alemania
Calificación del vendedor: 5 de 5 estrellas
Condición: New. PRINT ON DEMAND. Nº de ref. del artículo: 18397337879
Cantidad disponible: 4 disponibles
Imagen del vendedor
Study on the Effect of Grain Refiner
Publicado por
LAP LAMBERT Academic Publishing Sep 2022, 2022
ISBN 10: 6205499843
ISBN 13: 9786205499849
Nuevo
Taschenbuch
Librería: buchversandmimpf2000, Emtmannsberg, BAYE, Alemania
Calificación del vendedor: 5 de 5 estrellas
Taschenbuch. Condición: Neu. Neuware -Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490¿ for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm.Books on Demand GmbH, Überseering 33, 22297 Hamburg 52 pp. Englisch. Nº de ref. del artículo: 9786205499849
Cantidad disponible: 2 disponibles